Spec No.: JELF243C_9101E-01
No. Item
P6/14
Specification
Test method
7.5 Rated current
Product temperature rise: 25°C max.
Apply the rated current specified in chapter 3.
8. AEC-Q200 Requirement
8.1 Performance [based on table 5 for magnetics (inductors/transformer) AEC-Q200 Rev. D issued June 1,
2010]
AEC-Q200
Murata specification/deviation
No.
3
Stress
Test method
High
1000 h at 125°C
Set for 24 h at room condition, then
measured.
Meet table A after testing.
Table A
temperature
exposure
Appearance
No damage
Within ±10%
Inductance change rate:
0.6 nH to 30 nH (at 500 MHz)
33 nH to 120 nH (at 300MHz)
Substrate: 6-layers FR-4
4
Temperature
cycling
1000 cycles
-40°C to +125°C
Meet table A after testing.
Substrate: 6-layers FR-4
Set for 24 h at room condition, then
measured.
7
8
9
Biased humidity 1000 h at 85°C, 85% (RH). Unpowered. Meet table A after testing.
Set for 24 h at room condition, then
measured.
Substrate: 6-layers FR-4
Operational life Apply 125°C 1000 h
Meet table A after testing.
Substrate: 6-layers FR-4
Set for 24 h at room condition, then
measured.
External visual Visual inspection
No abnormalities
No defects
10 Physical
dimension
Meet chapter 5, "Appearance and
Dimensions".
12 Resistance to
solvents
Per MIL-STD-202
Method 215
Not applicable
13 Mechanical
shock
Per MIL-STD-202
Method 213
Meet table A after testing.
Substrate: 6-layers FR-4
Condition F:
1500 g’s (14.7 N), 0.5 ms, half sine
14 Vibration
5 g's (0.049 N) for 20 min, 12 cycles each Meet table A after testing.
of 3 orientations
Substrate: 6-layers FR-4
Test from 10 Hz to 2000 Hz
15 Resistance to
soldering heat
No-heating
Solder temperature
260°C±5°C
Pre-heating: 150°C±10°C, 60 s to 90 s
Meet table A after testing.
Immersion time 10 s
17 ESD
Per AEC-Q200-002
Per J-STD-002
ESD rank: Refer to chapter 3 ratings.
Substrate: 6-layers FR-4
18 Solderbility
Method b: not applicable
Pre-heating: 150°C±10°C, 60 s to 90 s
90% of the terminations is to be soldered.
19 Electrical
Measured: inductance
Per UL-94
No defects
characterization
20 Flammability
21 Board flex
Not applicable
Epoxy-PCB (1.6 mm)
Deflection 2 mm (min.)
Holding time 60 s
Meet table B after testing.
Murata deviation request:
Substrate: FR-4 (0.8 mm_thickness)
Holding time: 30 s
Table B
Appearance
No damage
Within ±10%
DC resistance change rate
22 Terminal
strength
Per AEC-Q200-006
A force of 17.7 N for 60 s
Murata deviation request: 2 N for 5 s
Substrate: 6-layers FR-4
No defects