SpecNo.JELF243A-0047W-01
P6/8
Reference Onl
11.2 Flux, Solder
・Use rosin-based flux.
Flux
・Don’t use highly acidic flux with halide content exceeding 0.2(wt)% (chlorine conversion value).
・Don’t use water-soluble flux.
・Use Sn-3.0Ag-0.5Cu solder
・Standard thickness of solder paste : 200μm to 300μm
Solder
Other flux (except above) Please contact us for details, then use.
11.3 soldering conditions (Reflow)
・Pre-heating should be in such a way that the temperature difference between solder and product surface is limited
to 150°C max. Cooling into solvent after soldering also should be in such a way that the temperature difference is
limited to 100°C max.
Insufficient pre-heating may cause cracks on the product, resulting in the deterioration of product quality.
・Standard soldering profile and the limit soldering profile is as follows.
The excessive limit soldering conditions may cause leaching of the electrode and / or resulting
in the deterioration of product quality.
Temp.
(℃)
260℃
230℃
Limit Profile
245℃±3℃
220℃
180
150
Standard Profile
30s~60s
60s max.
90s±30s
Time.(s)
Standard Profile
Limit Profile
Pre-heating
150~180°C 、90s±30s
Heating
above 220°C、30s~60s
245±3°C
above 230°C、60s max.
260°C, 10s
Peak temperature
Cycle of reflow
2 times
1 time
11.4 Reworking with soldering iron.
The following conditions must be strictly followed when using a soldering iron.
Pre-heating
150°C,1 min
350°C max.
80W max.
φ3mm max.
3(+1,-0)s
Tip temperature
Soldering iron output
Tip diameter
Soldering time
Times
2 times
Note : Do not directly touch the products with the tip of the soldering iron in order to prevent the crack on the products
due to the thermal shock.
11.5 Solder Volume
・Solder shall be used not to be exceeded the upper limits as shown below.
・Accordingly increasing the solder volume, the mechanical stress to Chip is also increased.
Exceeding solder volume may cause the failure of mechanical or electrical performance.
Upper Limit
Recommendable
1/3T≦t≦T
(T: Lower flange thickness)
T t
MURATA MFG.CO., LTD