3.振动
频率:10~55 Hz
无机械损伤
vibration
振幅:0.75 mm
电阻变化率:±2%
No substantial damage
方向和时间:X、Y 及 Z 轴各 2 小时
Frequency:10~55 Hz
Resistance change:within ±2%
Amplitude modulation:0.75 mm
Dirction and time:X、Y and Z direction for 2 hrs each
焊 锡 槽
4.可 焊 性
涂布面积:≥95%
Solder ability
温
度:245±5℃
Covered termination: ≥95%
Temperature: 245±5℃
时
间:3±0.5 s
Time: 3±0.5 s
5.耐焊接热
把引端浸入 260±5℃的焊锡 6mm 深,持续 5±1 秒时 电阻变化率:±2%
Solder ability
间,静置 24 小时后测试
Resistance change:within ±2%
the leadwinres shall be dipped in a molten solder of
260 ± 5 ℃ for ≤ 5 seconds up to the point
≥
6mm.after the specimen shall be left at room ambient
temperature for 24 hours,the resistance shall be
measured
6.高温放置
在 125±2℃中放置 1000+48 小时,静置 2 小时后测试 电阻变化率:
(高温保存)
0
±2%
Dry heat
Specimen shall be subjected to an ambient of 125± Resistance change:
2 ℃ for 1000+48hours.and after the specimen within ±2%
0
(high temperature storage)
shall be left at room ambient for 1 to 2 hours,the
resistance shall be measured
7.低温放置
(低温保存)
Cold
在-40±3℃中放置 1000+48 小时,静置 2 小时后测试 电阻变化率:
0
±2%
Specimen shall be subjected to an ambient of -40± Resistance change:
(low temperature
storage)
3℃
within ±2%
For 1000+48 hours.and after the specimen
0
shall be left at room ambient for 1 to 2 hours,the
resistance shall be measured
40±2℃ 90~95%RH,1000 hrs
8.稳态湿热
电阻变化率:±2%
Resistance change: within
±2%
humidity test
9.温度快速变化
-40℃/30ˊ —→
+125℃/30ˊ —→
25℃/5ˊ—→
25℃/5ˊ
电阻变化率:±2%
Resistance change: within
±2%
Temp Cycle test
循环五个周期
5 cycles
■
环保情况说明 Environmental Protection Statement
我司提供的所有热敏电阻物料均符合最新欧盟 ROHS 指令及 Reach 法规要求,请贵司放心使用。
We provide all materials conform to the requirements of the latest eu ROHS directive and the Reach regulation, please rest assured to use.