Product specification
7
11
NP0/X5RX7R
6.3V to 16V
01005
Surface-Mount Ceramic Multilayer Capacitors
TEST
TEST METHOD PROCEDURE
REQUIREMENTS
4.6
Capacitance shall be measured by the steps shown ∆C/C
Temperature
coefficient
in the following table.
Class1 (NP0):
±30ppm
The capacitance change should be measured after
5 min at each specified temperature stage.
Class 2: (X7R/X5R):
±15%
Step
Temperature(℃)
25±2
a
b
c
In case of applying voltage, the capacitance
change should be measured after 1 more min.
with applying
Lower temperature±3℃
25±2
voltage in equilibration of each temp. stage.
d
Upper Temperature± 2℃
25±2
e
CC0100MRX5R4(5)BB104(224):
0.2V±0.1Vrms
(1) Class I
Temperature Coefficient shall be calculated from
the formula as below
C2 - C1
Temp, Coefficient =
106 [ppm/℃]
C1xΔT
C1: Capacitance at step c
C2: Capacitance at 125℃
∆T: 100℃(=125℃-25℃)
Measuring Voltage: 0.5 to 5 Vrms
(2) Class II
Capacitance Change shall be calculated from the
formula as below
C2 - C1
∆C =
x 100%
C1
C1: Capacitance at step c
C2: Capacitance at step b or d
IEC 60384- 4.7
21/22
A force applied for 10 seconds to the line joining
the terminations and in a plane parallel to the
substrate
Force
size 01005 : 1N
Adhesion
4.8
Mounting in accordance with IEC 60384-22
paragraph 4.3
No visible damage
Bending
Strength
Conditions: bending 1 mm at a rate of 1 mm/s,
radius jig 5 mm
∆C/C
Class 1 (NP0):
within ±1% or 0.5 pF, whichever is greater
Class2 (X5R/X7R):
±10%
www.yageo.com
Jan. 18, 2017 V.9