HMC-MDB218
v02.1023
GaAs MMIC SUB-HARMONIC
IRM MIXER, 54 - 64 GHz
Mounting & Bonding Techniques for Millimeterwave GaAs MMICs
The die should be attached directly to the ground plane eutectically or with
conductive epoxy (see HMC general Handling, Mounting, Bonding Note).
0.102mm (0.004”) Thick GaAs MMIC
2
Wire Bond
50 Ohm Microstrip transmission lines on 0.127mm (5 mil) thick alumina
thin film substrates are recommended for bringing RF to and from the chip
(Figure 1). If 0.254mm (10 mil) thick alumina thin film substrates must be
used, the die should be raised 0.150mm (6 mils) so that the surface of
the die is coplanar with the surface of the substrate. One way to accom-
plish this is to attach the 0.102mm (4 mil) thick die to a 0.150mm (6 mil)
thick molybdenum heat spreader (moly-tab) which is then attached to the
ground plane (Figure 2).
0.076mm
(0.003”)
RF Ground Plane
Microstrip substrates should be placed as close to the die as possible in
order to minimize bond wire length. Typical die-to-substrate spacing is
0.076mm to 0.152 mm (3 to 6 mils).
0.127mm (0.005”) Thick Alumina
Thin Film Substrate
Figure 1.
Handling Precautions
Follow these precautions to avoid permanent damage.
0.102mm (0.004”) Thick GaAs MMIC
Storage: All bare die are placed in either Waffle or Gel based ESD protec-
tive containers, and then sealed in an ESD protective bag for shipment.
Once the sealed ESD protective bag has been opened, all die should be
stored in a dry nitrogen environment.
Wire Bond
0.076mm
(0.003”)
Cleanliness: Handle the chips in a clean environment. DO NOT attempt
to clean the chip using liquid cleaning systems.
RF Ground Plane
Static Sensitivity: Follow ESD precautions to protect against ESD strikes.
0.150mm (0.005”) Thick
Moly Tab
Transients: Suppress instrument and bias supply transients while bias is
applied. Use shielded signal and bias cables to minimize inductive pick-
up.
0.254mm (0.010”) Thick Alumina
Thin Film Substrate
Figure 2.
General Handling: Handle the chip along the edges with a vacuum collet
or with a sharp pair of bent tweezers. The surface of the chip has fragile air bridges and should not be touched with
vacuum collet, tweezers, or fingers.
Mounting
The chip is back-metallized and can be die mounted with AuSn eutectic preforms or with electrically conductive epoxy.
The mounting surface should be clean and flat.
Eutectic Die Attach: A 80/20 gold tin preform is recommended with a work surface temperature of 255 °C and a tool
temperature of 265 °C. When hot 90/10 nitrogen/hydrogen gas is applied, tool tip temperature should be 290 °C. DO
NOT expose the chip to a temperature greater than 320 °C for more than 20 seconds. No more than 3 seconds of
scrubbing should be required for attachment.
Epoxy Die Attach: Apply a minimum amount of epoxy to the mounting surface so that a thin epoxy fillet is observed
around the perimeter of the chip once it is placed into position. Cure epoxy per the manufacturer’s schedule.
Wire Bonding
RF bonds made with 0.003” x 0.0005” ribbon are recommended. These bonds should be thermosonically bonded
with a force of 40-60 grams. DC bonds of 0.001” (0.025 mm) diameter, thermosonically bonded, are recommended.
Ball bonds should be made with a force of 40-50 grams and wedge bonds at 18-22 grams. All bonds should be made
with a nominal stage temperature of 150 °C. A minimum amount of ultrasonic energy should be applied to achieve
reliable bonds. All bonds should be as short as possible, less than 12 mils (0.31 mm).
For price, delivery, and to place orders: Analog Devices, Inc., One Analog Way, Wilmington, MA 01887
Phone: 781-937-1428 • Order online at www.analog.com
2 - 6
Application Support: Phone: 1-800-ANALOG-D
5秒后页面跳转
PCF8574资料解读：主要参数分析、引脚说明
AD637数据手册解读：主要特性、引脚及其功能解读、电气参数
ADUM1201资料手册解读：参数分析、引脚说明、应用分析
一文带你了解压敏电阻器在直流电路中的过压保护作用
微信公众号
抖音公众号
浙公网安备 33010502006866号 浙ICP备10014259号-119
营业执照ICP证
数据手册
如果您发现信息不准确，