TCT Series AL Case
Data Sheet
Item
Performance
Test conditions (based on JIS C 5101−1 and JIS C 5101− 3)
As per 4.29 JIS C 5101-1
As per 4.13 JIS C 5101-3
Temperature
Stability
Temp.
∆C / C
Df (tan δ)
L.C.
−55°C
Within 0/−15% of initial value
Shall be satisfied the voltage on " Standard list "
−
Temp.
+85°C
∆C / C
Within +15/0% of initial value
Shall be satisfied the voltage on " Standard list "
5µA or 0.1CV whichever is greater
Df (tan δ)
L.C.
Temp.
∆C / C
Df (tan δ)
L.C.
+125°C
Within +20/0% of initial value
Shall be satisfied the voltage on " Standard list "
6.3µA or 0.125CV whichever is greater
There should be no significant abnormality.
As per 4.26JIS C 5101-1
Surge voltage Appearance
As per 4.14JIS C 5101-3
L.C.
Less than 200% of initial value
Within 20% of initial value
Less than 200% of initial limit
Apply the specified surge voltage every 5 0.5 min.
for 30 5 s. each time in the atmospheric condition of 85 2°C.
Repeat this procedure 1,000 times.
After the specimens, leave it at room temperature for
over 24h and then measure the sample.
∆C / C
Df (tan δ)
Loading at
High temperature
Appearance
L.C.
There should be no significant abnormality.
Less than 200% of initial limit
As per 4.23 JIS C 5101-1
As per 4.15 JIS C 5101-3
After applying the rated voltage for 2000+72/0 h without
discontinuation via the serial resistance of 3Ω or less
at a temperature of 85 2°C, leave the sample at room
temperature / humidity for over 24h and measure the value.
Within 20% of initial value
∆C / C
Df (tan δ)
Capacitance
Appearance
Less than 200% of initial limit
Terminal
strength
The measured value should be stable.
There should be no significant abnormality.
As per 4.35 JIS C 5101-1
As per 4.9 JIS C 5101-3
A force is applied to the terminal until it bends to 1mm and
by a prescribed tool maintain the condition for 5s.
(See the figure below)
(Unit : mm)
20
50
F (Apply force)
R230
1
thickness=1.6mm
45
45
www.rohm.com
c
2009.01 - Rev.G
○ 2009 ROHM Co., Ltd. All rights reserved.
4/6