Please read CAUTION and Notice in this catalog for safety. This catalog has only typical specifications. Therefore you are requested
to approve our product specification or to transact the approval sheet for product specification, before your ordering.
C02E8.pdf 01.7.26
Specifications and Test Methods
Specifications and Test Methods
Specification
No.
1
Item
Operating
Test Method
F5 : Y30°C to 85°C
Temperature Range
The rated voltage is defined as the maximum voltage which
may be applied continuously to the capacitor.
2
Rated Voltage
See the previous pages.
When AC voltage is superimposed on DC voltage, VP-P or VO-P
,
whichever is larger, shall be maintained within the rated voltage
range.
3
4
Appearance
Dimensions
No defects or abnormalities.
Visual inspection.
Using calipers.
Within the specified dimension.
No failure shall be observed when 250% of the rated voltage is
applied between the both terminations for 1 to 5 seconds, pro-
vided the charge/discharge current is less than 50mA.
5
Dielectric Strength No defects or abnormalities.
The insulation resistance shall be measured with a DC voltage
not exceeding the rated voltage at normal temperature and
humidity and within 2 minutes* of charging.
*5minutes for c>47µF.
Insulation
More than 10,000MΩ or 500Ω · F.
6
7
Resistance
(Whichever is smaller)
6
Capacitance
Within the specified tolerance.
The capacitance/D.F. shall be measured at 25°C at the fre-
quency and voltage shown in the table.
0.07 max. (50/100V)
0.09 max. (10/16/25V)
0.15 max. (6.3V)
Capacitance Frequency
Voltage
1±0.2Vrms
0.5±0.1Vrms
Dissipation Factor
(D.F.)
8
9
CV10µF
CG10µF
1±0.1kHz
120±24Hz
The capacitance change shall be measured after 5 min. at
each specified temperature stage.
The ranges of capacitance change compared to 25°C with the
temperature ranges shown in the table shall be within the spec-
ified ranges.
Capacitance
Temperature
Characteristics
Temp.
Range
Reference Cap. Change
Char.
Temp.
Rate
+22
°
°
F5 -30 to +85 C
25 C
Within
%
-82
Solder the capacitor on the testing jig (glass epoxy board)
shown in Fig.1 using a eutectic solder. Then apply 5N force in
parallel with the test jig for 10±1 sec. The soldering shall be
done either with an iron or using the reflow method and shall be
conducted with care so that the soldering is uniform and free of
defect such as heat shock.
No removal of the terminations or other defects shall occur.
c
Adhesive Strength
of Termination
b
a
10
Type
a
b
c
GJ218
GJ221
GJ231
GJ232
GJ243
1.0
1.2
2.2
2.2
3.5
3.0
4.0
5.0
5.0
7.0
1.2
1.65
2.0
2.9
3.7
Solder resist
Baked electrode or
copper foil
(in mm)
Fig.1
Solder the capacitor on the testing jig (glass epoxy board) in
the same manner and under the same conditions as (10).
The capacitor shall be subjected to simple harmonic motion
having a total amplitude of 1.5mm, the frequency being varied
uniformly between the approximate limits of 10 and 55Hz. The
frequency range, from 10 to 55Hz and return to 10Hz, shall be
traversed in approximately 1 minute. This motion shall be
applied for a period of 2 hours in each 3 mutually perpendicular
directions (total of 6 hours).
Item
Appearance
Capacitance Change Within the specified tolerance.
Frequency
No defects or abnormalities.
Vibration
Resistance
11
50, 100V 10, 16, 25V
0.07 max. 0.09 max. 0.15 max.
No failure
6.3V
D.F.
I.
Dielectric Strength
Continued on the following page.
31