RoHS
Multilayer Ferrite Beads
MLB03
0.039±0.004
(1.0±0.10)
Inches
Dimensions:
(mm)
0.020±0.004
(0.50±0.10)
0.020±0.004
(0.50±0.10)
0.010±0.004
(0.25±0.10)
0.016
(0.40)
0.016
0.018
(0.46)
(0.40)
Allied
Part
Number
Features
Impedance ( )
@ 100 MHz
DC
Resistance
(Ω) Max.
Ω
*Rated
Current
(mA)
• Surface mount EMI suppression components
• Nickel barrier termination for excellent resistance to solder heat
• Multi layer technology
+/- 25%
0.05
0.05
6
500
500
MLB03-060-RC
MLB03-100-RC
10
• Flow and reflow soldering
0.30
0.30
0.30
0.40
0.40
0.40
0.40
0.40
0.50
0.50
0.50
0.50
0.50
30
33
40
300
300
300
300
300
300
300
300
300
300
300
300
300
MLB03-300-RC
MLB03-330-RC
MLB03-400-RC
MLB03-470-RC
MLB03-600-RC
MLB03-700-RC
MLB03-750-RC
MLB03-800-RC
MLB03-900-RC
MLB03-101-RC
MLB03-121-RC
MLB03-151-RC
MLB03-221-RC
Electrical
47
60
Impedance Range: 6Ω to 1500Ω
70
Tolerance: 25% over entire range
Operating Range: -55ºC ~ +125ºC
75
80
90
100
120
150
220
Storage Temp: Under 25ºC at 40~60% Humidity
Rated Current: Based on temp rise not to exceed 30ºC
Resistance to Solder Heat
0.50
0.80
0.80
0.80
240
300
330
480
300
300
300
300
MLB03-241-RC
MLB03-301-RC
MLB03-331-RC
MLB03-481-RC
Pre-Heat 150ºC, 1 minute
Solder Composition: Sn/Ag3.0/Cu0.5
Solder Temp: 260±5ºC for 10sec ±1 sec.
Minimum of 75% of Electrode covered with new solder.
Impedance within 30% of initial value.
1.00
1.50
2.00
600
1000
1500
300
100
60
MLB03-601-RC
MLB03-102-RC
MLB03-152-RC
*Temperature rise∆T=30ºC at rated current.
All specifications subject to change without notice.
Test Equipment
(Z): HP4291A RF Impedance/Material Analyzer
(RDC): Chen Hwa 502BC
Physical
Packaging: 10000 per 7 inch reel.
Marking: None
www.alliedcomponents.com
714-665-1140
ALLIED COMPONENTS INTERNATIONAL
REVISED 6/18/09